Regon
Data sheet
| GRAMMATURA (ISO 9073.1) | 228 ± 23 g/mq |
| SPESSORE (ASTM D 1777) | 0,70 ± 0,10 mm |
| SPESSORE (ISO 9073.2) | 0,75 ± 0,10 mm |
| DENSITA | 326 mm |
| CARICO DI ROTTURA LONGITUDINALE (ISO 9073.3) | 300 ± 75 N |
| CARICO DI ROTTURA TRASVERSALE (ISO 9073.3) | 290 ± 70 N |
| ALLUNGAMENTO A ROTTURA LONGITUDINALE (ISO 9073.3) | 45 ± 10 % |
| ALLUNGAMENTO A ROTTURA TRASVERSALE (ISO 9073.3) | 72 ± 20 % |
| LACERAZIONE LONGITUDINALE (ISO 13937-2) | 28 ± 8 N |
| LACERAZIONE TRASVERSALE (ISO 13937-2) | 24 ± 8 N |
| MODULO 10% LONGITUDINALE (ISO 9073.3) | nd |
| MODULO 10% TRASVERSALE (ISO 9073.3) | nd |
| RETRAZIONE a 200°C/3′ LONGITUDINALE | -5,0 ± 2,0 % |
| RETRAZIONE a 200°C/3′ TRASVERSALE | -4,0 ± 1,6 % |
| COMPOSIZIONE | 58% PET + 42% legante |
| GRAMMATURA (ISO 9073.1) | 295 ± 30 g/mq |
| SPESSORE (ASTM D 1777) | 0,90 ± 0,11 mm |
| SPESSORE (ISO 9073.2) | 0,96 ± 0,11 mm |
| DENSITA | 328 mm |
| CARICO DI ROTTURA LONGITUDINALE (ISO 9073.3) | 460 ± 115 N |
| CARICO DI ROTTURA TRASVERSALE (ISO 9073.3) | 430 ± 110 N |
| ALLUNGAMENTO A ROTTURA LONGITUDINALE (ISO 9073.3) | 55 ± 13 % |
| ALLUNGAMENTO A ROTTURA TRASVERSALE (ISO 9073.3) | 85 ± 22 % |
| LACERAZIONE LONGITUDINALE (ISO 13937-2) | 40 ± 10 N |
| LACERAZIONE TRASVERSALE (ISO 13937-2) | 35 ± 7 N |
| MODULO 10% LONGITUDINALE (ISO 9073.3) | 140 ± 35 N |
| MODULO 10% TRASVERSALE (ISO 9073.3) | 70 ± 17 N |
| RETRAZIONE a 200°C/3′ LONGITUDINALE | -5,0 ± 2,0 % |
| RETRAZIONE a 200°C/3′ TRASVERSALE | -4,0 ± 1,6 % |
| COMPOSIZIONE | 41% PA + 17% PES + 42% LEGANTE |
| GRAMMATURA (ISO 9073.1) | 390 ± 40 g/mq |
| SPESSORE (ASTM D 1777) | 1,20 ± 0,12 mm |
| SPESSORE (ISO 9073.2) | 1,29 ± 0,12 mm |
| DENSITA | 325 mm |
| CARICO DI ROTTURA LONGITUDINALE (ISO 9073.3) | 640 ± 160 N |
| CARICO DI ROTTURA TRASVERSALE (ISO 9073.3) | 600 ± 150 N |
| ALLUNGAMENTO A ROTTURA LONGITUDINALE (ISO 9073.3) | 55 ± 13 % |
| ALLUNGAMENTO A ROTTURA TRASVERSALE (ISO 9073.3) | 95 ± 23 % |
| LACERAZIONE LONGITUDINALE (ISO 13937-2) | 60 ± 15 N |
| LACERAZIONE TRASVERSALE (ISO 13937-2) | 55 ± 13 N |
| MODULO 10% LONGITUDINALE (ISO 9073.3) | 200 ± 50 N |
| MODULO 10% TRASVERSALE (ISO 9073.3) | 95 ± 23 N |
| RETRAZIONE a 200°C/3′ LONGITUDINALE | -5,0 ± 2,0 % |
| RETRAZIONE a 200°C/3′ TRASVERSALE | -4,0 ± 1,6 % |
| COMPOSIZIONE | 41% PA + 17% PES + 42% LEGANTE |
| GRAMMATURA (ISO 9073.1) | 490 ± 45 g/mq |
| SPESSORE (ASTM D 1777) | 1,50 ± 0,14 mm |
| SPESSORE (ISO 9073.2) | 1,57 ± 0,14 mm |
| DENSITA | 327 mm |
| CARICO DI ROTTURA LONGITUDINALE (ISO 9073.3) | 830 ± 205 N |
| CARICO DI ROTTURA TRASVERSALE (ISO 9073.3) | 780 ± 190 N |
| ALLUNGAMENTO A ROTTURA LONGITUDINALE (ISO 9073.3) | 60 ± 15 % |
| ALLUNGAMENTO A ROTTURA TRASVERSALE (ISO 9073.3) | 95 ± 23 % |
| LACERAZIONE LONGITUDINALE (ISO 13937-2) | 75 ± 18 N |
| LACERAZIONE TRASVERSALE (ISO 13937-2) | 70 ± 17 N |
| MODULO 10% LONGITUDINALE (ISO 9073.3) | 270 ± 65 N |
| MODULO 10% TRASVERSALE (ISO 9073.3) | 115 ± 25 N |
| RETRAZIONE a 200°C/3′ LONGITUDINALE | -5,0 ± 2,0 % |
| RETRAZIONE a 200°C/3′ TRASVERSALE | -4,0 ± 1,6 % |
| COMPOSIZIONE | 41% PA + 17% PES + 42% LEGANTE |