NITTO 5703
Data sheet
| Tape thickness (EN 1942) | 0.30 mm |
| Adhesive type | Modified acrylic adhesive |
| Release liner type | PE-coated paper with green Nitto print (125 g/m²) |
| Carrier type | Anthracite polyolefine foam |
| Adhesion to BA steel (EN 1939) | 1400 cN/20mm |
| Release value (Nitto Belgium Test Method) | 40 cN/50mm |
| Static shear (EN 1943) | 1 mm/3h |
| Transport and storage conditions | Temperature 15 °C to 30 °C – Relative humidity 40 to 75% RH |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) PP | 50 mm/2h |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) ABS | 15 mm/2h |
| Tape thickness (EN 1942) | 0.40 mm |
| Adhesive type | Modified acrylic adhesive |
| Release liner type | PE-coated paper with green Nitto print (125 g/m²) |
| Carrier type | Anthracite polyolefine foam |
| Adhesion to BA steel (EN 1939) | 1600 cN/20mm |
| Release value (Nitto Belgium Test Method) | 40 cN/50mm |
| Static shear (EN 1943) | 1 mm/3h |
| Transport and storage conditions | Temperature 15 °C to 30 °C – Relative humidity 40 to 75% RH |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) PP | 30 mm/2h |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) ABS | 10 mm/2h |
| Tape thickness (EN 1942) | 0.60 mm |
| Adhesive type | Modified acrylic adhesive |
| Release liner type | PE-coated paper with green Nitto print (125 g/m²) |
| Carrier type | Anthracite polyolefine foam |
| Adhesion to BA steel (EN 1939) | 1600 cN/20mm |
| Release value (Nitto Belgium Test Method) | 40 cN/50mm |
| Static shear (EN 1943) | 1 mm/3h |
| Transport and storage conditions | Temperature 15 °C to 30 °C – Relative humidity 40 to 75% RH |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) PP | 40 mm/2h |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) ABS | 10 mm/2h |
| Tape thickness (EN 1942) | 0.90 mm |
| Adhesive type | Modified acrylic adhesive |
| Release liner type | PE-coated paper with green Nitto print (125 g/m²) |
| Carrier type | Anthracite polyolefine foam |
| Adhesion to BA steel (EN 1939) | 1600 cN/20mm |
| Release value (Nitto Belgium Test Method) | 50 cN/50mm |
| Static shear (EN 1943) | 1 mm/3h |
| Transport and storage conditions | Temperature 15 °C to 30 °C – Relative humidity 40 to 75% RH |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) PP | 35 mm/2h |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) ABS | 10 mm/2h |
| Tape thickness (EN 1942) | 1.1 mm |
| Adhesive type | Modified acrylic adhesive |
| Release liner type | PE-coated paper with green Nitto print (125 g/m²) |
| Carrier type | Anthracite polyolefine foam |
| Adhesion to BA steel (EN 1939) | 1700 cN/20mm |
| Release value (Nitto Belgium Test Method) | 50 cN/50mm |
| Static shear (EN 1943) | 1 mm/3h |
| Transport and storage conditions | Temperature 15 °C to 30 °C – Relative humidity 40 to 75% RH |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) PP | 10 mm/2h |
| Weight Added Peel Off (2h at 60 °C, width 20mm, 100g) ABS | 10 mm/2h |
| Saft test | 115 °C |
| Fogging | < 2 mg |
| Volatile Organic Compound | < 100 ppm |
| Formaldehyde content | < 1 ppm |